Multilayer Structure Comprising A Substrate and A Layer Of Silicon and Germanium Deposited Heteroepitaxially Thereon, and A Process For Producing It

ABSTRACT

A multilayer structure, comprises a substrate and a layer of silicon and germanium (SiGe layer) deposited heteroepitaxially thereon having the composition Si 1-x Ge x  and having a lattice constant which differs from the lattice constant of silicon, and a thin interfacial layer deposited on the SiGe layer and having the composition Si 1-y Ge y , which thin interfacial layer binds threading dislocations, and at least one further layer deposited on the interfacial layer.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The subject matter of the present invention is a multilayer structure, comprising a substrate and a layer of silicon and germanium (SiGe layer) deposited heteroepitaxially thereon and having a lattice constant which differs from a lattice constant of the substrate. Silicon which is deposited on a SiGe layer of this type is biaxially strained. Since the mobility of charge carriers in strained silicon is higher than in unstrained silicon, electronic components which make use of strained silicon to increase the switching speed are receiving more and more interest.

2. Description of the Related Art

In particular an SiGe layer, which consists of a mixture of silicon and germanium with a germanium content of from 20 to 50% and is as far as possible completely relaxed, is suitable for the deposition of strained silicon. Since the lattice constant of the SiGe layer is greater than that of silicon, the silicon lattice which is deposited on a layer of this type is widened, producing a layer of strained silicon.

In general, silicon is also used as a substrate for the relaxed SiGe layer to be deposited on. On account of the different lattice constants, a heteroepitaxial layer which grows is initially strained itself. The strain disappears beyond a critical layer thickness, forming dislocations. Misfit dislocations tend to continue in a plane along the direction of growth of the growing layer. However, threading dislocations are also formed as extensions of misfit dislocations. These threading dislocations extend in the direction of growth of the SiGe layer and reach as far as the surface of this layer. This occurs to an increased extent if the deposited SiGe layer is relaxed during a simple heat treatment (anneal). Threading dislocations should be avoided wherever possible, since they usually continue in layers which are deposited on the SiGe layer and disrupt the functioning of electronic components which are integrated in layers of this type. Pile-ups of threading dislocations are particularly harmful. Another important parameter for the quality of the SiGe layer is the roughness of the surface, which should be as low as possible. Misfit dislocations produce stress fields and lead to local differences in the growth rate during the growth of the SiGe layer, and ultimately to a surface topography, known as “cross-hatch” topography, which is likewise transferred to layers deposited on the SiGe layer. A measure of this cross-hatch is the RMS roughness of the surface, measured for example by AFM (Atomic Force Microscopy).

Strategies have already been developed for reducing the density of threading dislocations. One possible option is to increase the concentration of germanium in the SiGe layer in steps or continuously. Another approach pursues the objective of depositing the SiGe layer on a layer which has a high concentration of point defects. Misfit dislocations then tend to form closed dislocation loops, which lead through the area with the high concentration of point defects, rather than to lengthen into threading dislocations directed toward the surface of the SiGe layer. The density of the threading dislocations which still reach the surface of the substrate is of the order of magnitude of at least 1·10⁷ threading dislocations/cm² and is therefore still far too high for the material to be suitable for the fabrication of electronic components. US2004/0067644 A1 has described a process which allows the density of threading dislocations to be reduced to below 1·10⁵ threading dislocations/cm². The process substantially comprises etching the surface of the SiGe layer at the same time as the heat treatment which relaxes the SiGe layer (etch anneal process). An advantageous side-effect of so doing is that the surface roughness also decreases.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a multilayer structure and a simple process for producing it, in which the surface of the structure has a low roughness and a low density of threading dislocations and pile-ups of threading dislocations.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1 and 2 illustrate the layered structures of the present invention by cross-sectional Transmission Electron Microscopy.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT(S)

The subject matter of the invention is a multilayer structure, comprising a substrate and a layer of silicon and germanium (SiGe layer) deposited heteroepitaxially thereon having the composition Si_(1-x)Ge_(x) and having a lattice constant which differs from the lattice constant of silicon, which multilayer structure includes a thin interfacial layer deposited on the SiGe layer and having the composition Si_(1-y)Ge_(y), which thin interfacial layer binds threading dislocations, and at least one further layer deposited on the interfacial layer.

The surface of the multilayer structure is distinguished by a particularly low density of threading dislocations and pile-ups of threading dislocations and by a low roughness. A particular feature of the multilayer structure is an interfacial layer of silicon and germanium which binds threading dislocations at the interface with the SiGe layer below. As a result, a considerably smaller number of threading dislocations reaches the surface of the interfacial layer and of the at least one further layer deposited thereon.

The subject matter of the invention is also a process for producing a multilayer structure, comprising the steps of providing a layer of silicon and germanium (SiGe layer) deposited heteroepitaxially on a substrate, having the composition Si_(1-x)Ge_(x), and having a lattice constant which differs from the lattice constant of silicon; and depositing a thin interfacial layer having the composition Si_(1-y)Ge_(y) (“subsequent” SiGe layer) on the previously deposited SiGe layer, which thin interfacial layer binds threading dislocations, and depositing at least one further layer on the interfacial layer.

The SiGe layer may be strained or relaxed. The SiGe layer may have a constant concentration Si_(1-x)Ge_(x) of silicon and germanium. However, it is preferably a layer in which the concentration of germanium increases in steps or continuously over the thickness of the layer (graded layer) and only reaches the concentration Si_(1-x)Ge_(x) at the surface of the layer. The index x preferably has a value of from 0.2 to 0.5.

The SiGe layer is preferably present on a surface of silicon as substrate, most preferably on a semiconductor wafer of silicon or an SOI layer structure (silicon on insulator) with a silicon layer and an oxide layer beneath it.

According to the invention, a thin interfacial layer is deposited on the SiGe layer; this interfacial layer binds threading dislocations at the interface with the SiGe layer, so that the density of these threading dislocations at the surface of the multilayer structure is reduced considerably compared to the density of the threading dislocations on the surface of the SiGe layer. The threading dislocation density (TDD) on the surface of the multilayer structure is at most 1.5 E+4 threading dislocations/cm², preferably less than 5 E+3 threading dislocations/cm². The density of pile-ups of threading dislocations (PuD) is preferably at most 1 cm/cm². The roughness of the surface of the multilayer structure is preferably at most 2 Å rms (1 μm×1 μm measurement window). The thickness of the interfacial layer is preferably from 2 to 30 nm. If the thickness of the interfacial layer is below the lower limit of the preferred thickness range or above the upper limit, this has an adverse effect on the roughness of the surface of the interfacial layer and therefore also on the surface of the multilayer structure. The interfacial layer has a substantially constant composition Si_(1-y)Ge_(y), where the index y may preferably assume the same values as the index x.

To deposit the interfacial layer, the SiGe layer is exposed to a gaseous mixture which contains hydrogen, a hydrogen halide compound, a silicon compound and a germanium compound. This is preferably done in an epitaxy reactor. The concentrations of the gaseous compounds are set in such a way that net deposition of material of the composition Si_(1-y)Ge_(y) takes place under the selected temperature and pressure conditions. The deposition is preferably carried out at a temperature of between 900 and 1100° C. and at atmospheric pressure or a lower pressure. The deposition rate is greater than 0 nm/min and is preferably at most 50 nm/min.

Suitable silicon compounds include SiH₄ and chlorosilanes, among which dichlorosilane is preferred. Suitable germanium compounds are chlorogermanes and alkyl derivatives thereof, as well as GeH₄. GeH₄, GeCl₄ and CH₃GeCl₃ are particularly preferred. The ratio of silicon compound to germanium compound in the gas atmosphere used for deposition of the interfacial layer is set in such a way that the growing interfacial layer has the desired composition Si_(1-y)Ge_(y). The preferred hydrogen halide compound in the gas atmosphere is HCl. The ratio of hydrogen halide compound, on the one hand, and silicon compound and germanium compound, on the other hand is preferably in the range from 100:1 to 1:1. On account of the low density of threading dislocations on the surface and the low roughness of the surface of the interfacial layer, it is particularly preferable for a layer of strained silicon to be deposited as a further layer directly on the surface of the interfacial layer. Nevertheless, it is also possible for one or more further layers to be deposited in advance. By way of example, a relaxed heteroepitaxial layer with a constant composition Si_(1-z)Ge_(z) can be deposited on the interfacial layer as buffer layer before the layer of strained silicon; the index z may in this case preferably assume the same values as the index y. The degree of relaxation of the buffer layer is preferably greater than 90%. The buffer layer has a thickness of preferably 0.5 to 2 μm.

Comparative Example

Silicon substrate wafers were treated at a reduced pressure in a single-wafer epitaxy reactor. The following process steps were carried out:

-   Step 1. Loading of the reactor. -   Step 2. Heat treatment of the substrate wafer under hydrogen (H₂     bake) at a temperature of 1120° C. -   Step 3. Deposition of an SiGe layer with an increasing germanium     content (graded layer) (0-20%) at a temperature of 800-900° C. -   Step 4. Deposition of a buffer layer of silicon and germanium with a     constant germanium content of 20% (constant composition layer) and a     thickness of 1 μm. -   Step 5. Deposition of an 18 nm thick layer of strained silicon at a     temperature of 700° C. -   Step 6. Unloading of the multilayer structure from the reactor.

EXAMPLE

Further substrate wafers of the same type as that of the Comparative Example were treated in the same reactor as in the Comparative Example, with one difference:

-   Steps 1 to 3: as in the Comparative Example -   Step 4: Deposition of an interfacial layer of silicon and germanium     with a constant germanium content of 20% by introducing a mixture of     hydrogen chloride, dichlorosilane and germane at a temperature of     1050 ° C. -   Steps 5 to 7: same as steps 4 to 6 in the Comparative Example

Examination of the multilayer structures formed: the interfacial layer examination was carried out by cross-sectional TEM (Transmission Electron Microscopy, X-TEM). FIG. 1 clearly shows the interfacial layer between graded layer (with dislocation network) and constant composition layer. The thickness of the interfacial layer is approx. 2 to 3 nm. FIG. 2 shows how dislocations from the lower-lying SiGe layer are absorbed in the interfacial layer. The dislocations then run within the plane of the boundary between the SiGe layer and the interfacial layer and do not grow further into the buffer layer.

The deposition of the interfacial layer leads to a reduction in the threading dislocation density (TDD), in particular the pile-up density (PuD) of such dislocations, and to a reduction in the RMS roughness as a result of elimination of the crosshatch structure. The morphology of the surface can be influenced by changing the process conditions within wide ranges during the deposition of the interfacial layer.

Comparative Example Example TDD/cm − 2 4E+5 1.3E+4 PuD/cm − 1 18 1.0 RMS 40 μm × 40 μm  6.5 nm  1.6 nm RMS 1 μm × 1 μm 0.42 nm 0.14 nm

While embodiments of the invention have been illustrated and described, it is not intended that these embodiments illustrate and describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention. 

1. A multilayer structure, comprising a substrate and a layer of silicon and germanium (SiGe layer) deposited heteroepitaxially thereon having the composition Si_(1-x)Ge_(x) and having a lattice constant which differs from the lattice constant of silicon, the multilayer structure having a thin interfacial layer which binds threading dislocations deposited on the SiGe layer, the thin interfacial layer having the composition Si_(1-y)Ge_(y), and having a thickness of from 2 nm to 30 nm, and at least one further layer deposited on the thin interfacial layer.
 2. The multilayer structure of claim 1, wherein the concentration of germanium increases over the thickness of the SiGe layer.
 3. The multilayer structure of claim 1, which has an interfacial layer thickness of from about 2 nm to about 3 nm.
 4. The multilayer structure of claim 1, having a density of at most 1.5 E+4 threading dislocations/cm² on the surface.
 5. The multilayer structure of claim 1, having a density of at most 1 cm/cm² pile-ups of threading dislocations.
 6. The multilayer structure of claim 1, which has a surface roughness of at most 2 Å rms in a 1 μm×1 μm window.
 7. The multilayer structure of claim 1, which includes a relaxed heteroepitaxial buffer layer having the composition Si_(1-z)Ge_(z), which has been deposited on the thin interfacial layer, and a layer of strained silicon, which has been deposited on the relaxed heteroepitaxial buffer layer having the composition Si_(1-z)Ge_(z).
 8. The multilayer structure of claim 1, which includes a layer of strained silicon which has been deposited on the thin interfacial layer. 9.-20. (canceled)
 21. The multilayer structure of claim 1, wherein x and y are equal, and the thin interfacial layer is deposited at a rate of ≦50 nm/min. at a temperature of 900 to 1100° C.
 22. A multilayer structure, comprising a substrate and a layer of silicon and germanium (SiGe layer) deposited heteroepitaxially thereon having the composition Si_(1-x)Ge_(x) and having a lattice constant which differs from the lattice constant of silicon, the multilayer structure having a thin interfacial layer which binds threading dislocations deposited on the SiGe layer, the thin interfacial layer having the composition Si_(1-y)Ge_(y) and having a thickness of from 2 nm to 30 nm, and at least one further layer deposited on the thin interfacial layer produced by a process comprising the steps of: providing a layer of silicon and germanium (SiGe layer) deposited heteroepitaxially on a substrate having the composition Si_(1-x)Ge_(x) and having a lattice constant which is different from the lattice constant of silicon, and depositing a thin interfacial layer having the composition Si_(1-y)Ge_(y) on the SiGe layer, which thin interfacial layer binds threading dislocations, and depositing at least one further layer on the interfacial layer. 